Fine pearlite and a small amount of marten site are found in quenched 1080 steel. What microstructure would be expected if we used a low-alloy, 0.2% C steel? What microstructure would be expected if we had used a 4340 steel? [See Figures 13-14, 13-15, and 13-16(b).]