According to the matte mode, copper plating matte melting is one of the basic steps of the step process. In the matte melting process, two phases are formed, copper-rich (matt) and iron-rich (slag). These phases are separated due to the property of the furnace. The slag accumulates just above the matte phase, while the denser matte disperses under the furnace. Within the framework of this information: after a matte melting; Calculate the terminal precipitation of a 100 micron diameter matte droplet in the liquid slag in the 30%SiO2-70%FeO mixture. If the slag depth is 0.6 m, how long does it take for this droplet to reach the matte phase? Matinee Density: 4100 kg m Density of Slag: 3500 kg m3 Viscosity of Slag: 0.2 kg m sec Matine Viscosity: 0.9 kg m sec

Mat moduna gre bakr retiminde mat ergitmesi adm prosesin temel admlarndan biridir. Mat ergitme ileminde bakrca zengin (mat) ve demirce zengin (curuf) olmak zere iki faz meydana gelir. Oluan bu fazlar firn iersinde younluk farkndan dolay ayrlr. Daha youn olan mat furnn altnda toplanrken, curuf mat faznn hemen stnde birikir. Bu bilgiler erevesinde: bir mat ergitmesi sonrasinda; 100 micron apndaki mat damlacn %30SiO2%70FeO bileimindeki sv curuf ierisindeki terminal kme hzn hesaplaynz. Curuf derinlii 0,6m ise bu damlack mat fazna ne kadar srede ular? Mat moduna gre bakr retiminde mat ergitmesi adm prosesin temel admlarndan biridir. Mat ergitme ileminde bakrca zengin (mat) ve demirce zengin (curuf) olmak zere iki faz meydana gelir. Oluan bu fazlar firn iersinde younluk farkndan dolay ayrlr. Daha youn olan mat furnn altnda toplanrken, curuf mat faznn hemen stnde birikir. Bu bilgiler erevesinde: bir mat ergitmesi sonrasinda; 100 micron apndaki mat damlacn %30SiO2%70FeO bileimindeki sv curuf ierisindeki terminal kme hzn hesaplaynz. Curuf derinlii 0,6m ise bu damlack mat fazna ne kadar srede ular