Question: For a continuous and oriented fiber - reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 1 9 . 7 and

For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are
19.7 and and {:5.3\times 10^(5)\psi ), respectively. If the volume fraction of fibers is 0.44, determine the moduli of elasticity of
fiber and matrix phases.
E_(m)=,GPa
E_(f)=,GPa
For a continuous and oriented fiber - reinforced

Step by Step Solution

There are 3 Steps involved in it

1 Expert Approved Answer
Step: 1 Unlock blur-text-image
Question Has Been Solved by an Expert!

Get step-by-step solutions from verified subject matter experts

Step: 2 Unlock
Step: 3 Unlock

Students Have Also Explored These Related Mechanical Engineering Questions!

Q:

For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 and 3.66GPa (2.8 ( 106 and 5.3 ( 105psi), respectively. If...

Q:

For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 and 3.66 GPa (2.8 106 and 5.3 105 psi), respectively. If...

Q:

Current Attempt in Progress Incorrect. For a continuous and oriented fiber - reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 1 9 . 7 and and 5 . 3 1 0...

Q:

For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 33.1 and 3.66 GPa (4.8 106 and 5.3 105 psi), respectively. If...

Q:

Hmwrk 8 no 4 Current Attempt in Progress For a continuous and oriented fiber - reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 1 9 . 7 and 3 . 6 6 GPa...

Q:

1 6 . 1 0 For a continuous and oriented fiberreinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 3 3 . 1 and and ( : 5 . 3 1 0 5

Q:

A continuous and aligned fibrous reinforced composite having a cross-sectional area of 970 mm2 (1.5 in.2) is subjected to an external tensile load. If the stresses sustained by the fiber and matrix...

Q:

4 . A continuous and aligned fibrous reinforced composite having a cross - sectional area of \ ( 5 0 0 \ mathrm { ~mm } ^ { 2 } \ ) is subjected to an external tensile load of \ ( 7 8 , 0 0 0 \...

Q:

A continuous and aligned fibrous reinforced composite having a cross - sectional area of \ ( 1 , 1 1 0 \ mathrm { ~mm } ^ { 2 } \ ) is subjected to an external tensile load. If the stresses sustained...

Q:

2 - For a continuous and oriented fiber - reinforced composite, the moduli of elasticity of the fiber and matrix are 8 5 and 2 0 GPa, respectively. If the volume fraction of fibers is 0 . 3 0 ,...

Q:

This table shows the staffing and pay rates of the Marshall City Fire Department: Employee Grade Number in Grade Salary Chief 1 $105,000 Shift Commander 3 70,000 Firefighter 1 12 39,000 Firefighter 2...

Q:

Of the following, which is the least reliable type of audit evidence? Confirmations mailed by outsiders to the auditors. Correspondence between the auditors and suppliers. Copies of sales invoices...

Q:

What is a processing department production report?Group of answer choices A. A budget prepared by the cost accountant to estimate the total production costs for a particular processing department. B....

Q:

Debate 4-3 Positive versus Normative Accounting Theory A comprehensive theory of accounting has yet to be developed. Team Debate Team 1: Present arguments that support reliance on positive theory to...