A manufacturer is successfully hot forging a certain part, using material supplied by Company A. A new supply of material is obtained from Company B, with the same nominal composition of the major alloying elements as that of the material from Company, However, it is found that the new forgings are crack even though the same procedure is followed as before what is the probable reason?