Is it possible to produce a continuous and oriented aramid fiber-epoxy matrix composite having longitudinal and transverse moduli of elasticity of 35 GPa (5 × 106 psi) and 5.17 GPa (7.5 × 105 psi), respectively? Why or why not? Assume that the elastic modulus of the epoxy is 3.4 GPa (4.93 × 105 psi).