Question: Current Attempt in Progress The yield strength of a brass alloy that has an average grain diameter of 0 . 0 1 mm is 1

Current Attempt in Progress
The yield strength of a brass alloy that has an average grain diameter of 0.01 mm is 160 MPa ; at a grain diameter of 0.065 mm the yield strength is 75 MPa . Compute the yield strength for this same alloy when the average grain diameter is 0.10 mm .
y=
MPa
Current Attempt in Progress The yield strength of

Step by Step Solution

There are 3 Steps involved in it

1 Expert Approved Answer
Step: 1 Unlock blur-text-image
Question Has Been Solved by an Expert!

Get step-by-step solutions from verified subject matter experts

Step: 2 Unlock
Step: 3 Unlock

Students Have Also Explored These Related Mechanical Engineering Questions!

Q:

Marjorie, a 17-year old high school student, lives with her parents. She she decided to join a gym to get into shape. She entered into a one-year contract with Basic Fitness, LLC, under which she had...

Q:

The yield strength for an alloy that has an average grain diameter of 5.0 102 mm is 115 MPa. At a grain diameter of 6.0 103 mm, the yield strength increases to 237 MPa. At what grain diameter, in mm,...

Q:

*The answer is NOT 0.055 mm or 0.0183 mm* The yield strength for an alloy that has an average grain diameter of 5.5102mm is 143MPa. At a grain diameter of 8.1103mm, the yield strength increases to...

Q:

The yield strength for an alloy that has an average grain diameter of 4.5102mm is 131MPa. At a grain diameter of 7.7103mm, the yield strength increases to 276MPa. At what grain diameter, in mm, will...

Q:

The yield strength for an alloy that has an average grain diameter of 5 . 3 1 0 - 2 m m is 1 3 2 MPa. At a grain diameter of 7 . 3 1 0 - 3 m m , the yield strength increases to 2 6 3 MPa. At what...

Q:

The yield strength for an alloy that has an average grain diameter of 5.5102mm is 143MPa. At a grain diameter of 8.1103mm, the yield strength increases to 246MPa. At what grain diameter, in mm, will...

Q:

Grain diameter = 0.01 mm Time = 1 min 850C 800C 1.0 700C Grain diameter (mm) (Logarithmic scale) o 600C 0.1 500C O 0.01 10 103 104 102 Time (min) (Logarithmic scale) Question 4 of 5 - /1 e View...

Q:

For many metals the average grain diameter (d) as a function of time (t) during grain growth at elevated temperatures is described by the following empirical Grain Growth law: d^2-d0^2 = Kt Also for...

Q:

(a) From the plot of yield strength versus (grain diameter) ?1/2 for a 70 Cu?30 Zn cartridge brass, Figure, determine values for the constants ? 0 and k y in Equation 7.7. (b) Now predict the yield...

Q:

1. (a) From the plot of yield strength versus (grain diameter) 1/2 for a 70 Cu30 Zn cartridge brass, Figure below, determine values for the constants 0 and k y in the HP equation. . (b) Now predict...

Q:

Why do we focus on cash flows rather than accounting profits in making our capital- budgeting decisions? Why are we interested only in incremental cash flows rather than total cash flows?

Q:

A rectangle has sides with lengths 18 units and 11 units. Find the angle to one decimal place between the diagonal and the side with length of 18 units. Hint: Set up a rectangular coordinate system,...

Q:

IAS 3 8 - Intangible Assets - was primarily issued in order to identify the criteria that need to be present before expenditure on intangible items can be recognized as an asset. The standard also...

Q:

Question 1:John Company uses LIFO inventory valuation method and reportsthe following:2019 Assets2019 Inventory2019 LIFO Reserve2018 LIFO Reserve$88,080$5,664$6,450$4,350Assume a ta 1 answer