Temperature (C) 12. Mg-20 wt% Sn alloy is cooled from 700C. By drawing the diagram on...

Transcribed Image Text:

Temperature (C) 12. Mg-20 wt% Sn alloy is cooled from 700C. By drawing the diagram on your paper, For this alloy, a) Determine the starting temperature of solidification. b) Determine the composition and amount of each phase at 400C. 800 L 700 B+L 600 a+L 561.2C a 14.85 37.6 70.6 500 B+L 400 300 a+B L + Sn 203.5C 200 97.9 B 100 + Sn Mg 20 40 60 80 Sn Weight percent tin 13. a) How can you explain the term of age hardening process? Please explain stages and give detailed information by giving an example. b) What is the difference between precipitation and dispersion strengthened alloys? 14. Explain why, under some circumstances, it is not advisable to weld a structure that is fabricated with a 3003- aluminum alloy. Hint: strengthening of a 3003 alloy is accomplished by cold working. 15. Using the isothermal transformation curve shown to the right for the Fe-C system, determine the final structure of the Fe-C alloy for the following cooling processes (assume all processes start as homogeneous austenite above 760 C): a) Rapidly cool to 600 C, hold for 102 second, rapidly cool to room temperature; emperature (C) 800 Eutectoid temperature 1400 700 600 500 400 1200 1000 800 b) Rapidly cool to 350C, hold for 102 seconds, rapidly cool to room temperature; 300 600 M(start) 200 50% M+A 400 M(50%) M(90%) 100 200 c) Rapidly cool to 300 C, hold for 10 seconds, rapidly cool to room temperature. 10-1 1 10 102 103 104 105 Time (s) Temperature (F) Temperature (C) 12. Mg-20 wt% Sn alloy is cooled from 700C. By drawing the diagram on your paper, For this alloy, a) Determine the starting temperature of solidification. b) Determine the composition and amount of each phase at 400C. 800 L 700 B+L 600 a+L 561.2C a 14.85 37.6 70.6 500 B+L 400 300 a+B L + Sn 203.5C 200 97.9 B 100 + Sn Mg 20 40 60 80 Sn Weight percent tin 13. a) How can you explain the term of age hardening process? Please explain stages and give detailed information by giving an example. b) What is the difference between precipitation and dispersion strengthened alloys? 14. Explain why, under some circumstances, it is not advisable to weld a structure that is fabricated with a 3003- aluminum alloy. Hint: strengthening of a 3003 alloy is accomplished by cold working. 15. Using the isothermal transformation curve shown to the right for the Fe-C system, determine the final structure of the Fe-C alloy for the following cooling processes (assume all processes start as homogeneous austenite above 760 C): a) Rapidly cool to 600 C, hold for 102 second, rapidly cool to room temperature; emperature (C) 800 Eutectoid temperature 1400 700 600 500 400 1200 1000 800 b) Rapidly cool to 350C, hold for 102 seconds, rapidly cool to room temperature; 300 600 M(start) 200 50% M+A 400 M(50%) M(90%) 100 200 c) Rapidly cool to 300 C, hold for 10 seconds, rapidly cool to room temperature. 10-1 1 10 102 103 104 105 Time (s) Temperature (F)