Type 304L stainless steel containing 0.02% C shows intergranular corrosion (IGC) after exposure to hot corrosive gases
Fantastic news! We've Found the answer you've been seeking!
Question:
Type 304L stainless steel containing 0.02% C shows intergranular corrosion (IGC) after exposure to hot corrosive gases at 600°C for 7 days. How can this be, since the alloy is normally resistant to IGC because of its low carbon content? How could this attack be prevented, still using austenitic stainless steel?